Usage: | Planting Material, Denture Processing |
---|---|
Usage Times: | Disposable |
Material: | Ceramics |
Applicable Departments: | Dental Department |
Nature: | Denture Processing |
Certification: | CE, FDA Sfds Rfda |
Proveedores con licencias comerciales verificadas
El tema | HS | HT | ST | ST-C | ST-M | UT-M | UT | Multicapa en 3D. |
Fuerza de flexión | 1470Mpa | 1470 Mpa | 1200 Mpa | 1200 Mpa | 1200 Mpa | 1100 Mpa | 1100 Mpa | >1200 Mpa |
Transmitancia | Opaco | El 30% | El 41% | El 40% | El 40% | El 45% | El 45% | El 49% |
La densidad de sinterización pre (g/cm3). | 3.20 | 3.20 | 3.15. | 3.20 | 3.20 | 3.25 | 3.25 | 3.25 |
Vicker's dureza (MPA) | 1400 | 1400 | 1300 | 1350 | 1350 | 1250 | 1250 | 1250 |
Factor de contracción(%) | 19-22 | 19-22 | 19-22 | 19-22 | 19-22 | 19-22 | 19-22 | 19-22 |
La temperatura de sinterización | 1460 °C. | 1460 °C. | 1530 °C. | 1530 °C. | 1530 °C. | 1530 °C. | 1530 °C. | 1480 °C. |