MIM polvo de acero inoxidable | |||||||||||
El grado | Composición química (wt%) | ||||||||||
C | Cr | Ni | Mn | Mo | Cu | N.b. | S | P | Si | O. | |
316L | ≤0,03 | 16-18 | 10-14 | ≤2 | 2-3 | - | - | ≤0,03 | ≤0,035 | ≤1 | ≤0.4 |
316 | ≤0,08 | 16-18 | 10-14 | ≤2 | 2-3 | - | - | ≤0,03 | ≤0,035 | ≤1 | ≤0.4 |
304L | ≤0,03 | 18-20 | 8-12 | ≤2 | - | - | - | ≤0,03 | ≤0,035 | ≤1 | ≤0.4 |
304 | ≤0,08 | 16-18 | 8-12 | ≤2 | - | - | - | ≤0,03 | ≤0,045 | ≤1 | ≤0.4 |
17-4PH | ≤0,07 | 15.5-17.5 | 3-5 | ≤1 | - | 3-5 | 0.15-0.45 | ≤0,03 | ≤ 0.040 | ≤1 | ≤0.4 |
420 | 0,3-0,4 | 12-14 | 0.4-0.6 | ≤1 | ≤0,75 | - | - | ≤0,03 | ≤ 0.040 | ≤1 | ≤0.4 |
440C | 0.95-1.2 | 16-18 | ≤0.6 | ≤1 | ≤0,75 | - | - | ≤0,03 | ≤ 0.040 | ≤1 | ≤0.4 |
Granulometría (μm) | Toca la densidad(g/cm3). | ||||||||||
D90 | D50 | D10 | - | ||||||||
GZSL-1 | ≤22.0 | 7.0-8.0 | 2.0-2.5 | 4.6 | |||||||
GZSL-2 | 26.0 | 8.5-9.5 | 2,5-3,0 | 4.7 | |||||||
Otras cosas | Podemos ser personalizados de acuerdo a sus necesidades. |
El grado | Ifm (g/10 min) | La inyección de temperatura (ºC) | Temperatura del molde (ºC) | OSF | La relación Debinding (%) | La densidad de color verde (g/cm3). | La densidad de sinterizado (g/cm3). |
316L | 800-1500 | 190 | 110 | 1.167 | ≥7,9 | 5.35-5.42 | 7.8 |
304L | 800-1500 | 5.35-5.41 | 7.8 | ||||
17-4PH | 800-1500 | 5.29-5.35 | 7.7 |
El grado | La sinterización | Límite de fluencia | Fuerza tensil | La elongación | La dureza | Resistencia a la corrosión |
316L | ≥7.80 g/cm3 | 184 MPa | 542 MPa | El 64% | 80 HRB | 72h |
17-4PH | ≥7.70 g/cm3 | 802 MPa | 854 MPa | El 8,5% | 30 HRC. | 24h |