ZC-3241 Silane XLPE Black Insulation Compound for Aerial Insulated Cable up to 10kV
It is a one-step silane polyethylene insulating material, a crosslinking polyethylene insulation material prepared by a special process, using high-quality polyethylene resin, silane coupling agent, initiator, catalyst, antioxidant and other additives. It is used as insulation of aerial insulated cable up to 10 kV. It has excellent extrusion performance, stable & reliable physical and chemical indicators.
| Product |
Silane XLPE
insulation compounds |
| Product code |
3201 |
3211 |
3232 |
3241 |
3251 |
| Description |
Sioplas 3kV |
Sioplas 10kV |
Monosil 3kV |
Monosil 10kv |
Monosil 10kv |
| Standard |
Test Method |
|
|
|
|
|
| Density(g/cm³) |
ASTM D792 |
0.92±0.01 |
0.92±0.01 |
0.92±0.01 |
0.92±0.01 |
|
| Tensile strength(Mpa) |
IEC 60811-1-1 |
20.0 |
18.5 |
20.0 |
18.5 |
22.0 |
| Elongation at break (%) |
600 |
460 |
520 |
510 |
640 |
| MFI 2.16kg &190ºC (g/10min) |
ASTM D1238 |
1 |
0.8 |
|
|
|
| Ageing Behavior |
Tensile strength variation (%) |
IEC 60811-1-2 |
+5 |
+5 |
+7 |
+5 |
+6 |
| Elongation variation (%) |
-6 |
-6 |
-6 |
-6 |
-7 |
| Hot set @200ºC 15min, 0.2Mpa |
Elongation under the load(%) |
IEC 60811-2-1 |
60 |
50 |
60 |
50 |
60 |
| Permanent deformation after cooling(%) |
-3 |
-3 |
0 |
-3 |
0 |
| Gel content(%) |
ASTM D2765 |
65 |
|
65 |
|
|
| Low temperature bittleness @-76ºC |
ASTM D746 |
(0/30)pass |
(0/30)pass |
(0/30)pass |
(0/30)pass |
(0/30)pass |
| Volume resistivity (Ω·cm) |
IEC 60093 |
1x1015 |
6x1014 |
1x1015 |
5x1014 |
6x1014 |
| Dielectric strength(MV/m) |
IEC 60243-1 |
38 |
37 |
38 |
37 |
30 |
| Dissipation factor 20ºC, 50HZ |
IEC 60250 |
2x10-4 |
2x10-4 |
2x10-4 |
2x10-4 |
5x10-5 |
| Dielectric constant 20ºC, 50HZ |
IEC 60250 |
1.7 |
1.7 |
1.7 |
1.7 |
|
Typical values in the table are measured under the condition that the material is fully crosslinked, and if suficient crosslinking is not achieved, the performance of the material may be different.
Processing:
it is recommended to use a conventional extruder (three-layer co-extrusion, length-diameter ratio of 20:1 to 30:1)for operation, and other equipment needs to be adjusted according to the situation.
| Zone |
Feeding Section |
Compression Section |
Homogenization Section |
Model Section |
| Temperature RangeºC |
160-180 |
180-200 |
200-210 |
210-220 |
- Above temperature is only for reference. It is recommended that customers adjust according to the temperature control of their respective equipment, the current at the time of extrusion, the melting pressure and the actual situation after the cable extrusion.
Product packing:
Vacuum packing in aluminum foil bags. The net weight of each bag is 25+0.05 kg.
Note:
1. Before usina, it is necessary to confirm that the package are sealed intactlv, The product should not beexposed to air for a long time, lf not, the hot prolongation performance will be affected.2. Transportation, stacking and storage should prevent sun, rain and water immersion, etc, and the storageenvironment should be clean, dry and ventilated.
Production Workflow Chart
Nanjing Zhongchao New Materials Corporation is a leading polyolefin compounds manufacturer in the power and telecommunication industry since its establishment in 2011. We garnered clients worldwide, earning Export Excellence Award and showcasing our international success. Our commitment to green innovation and delivering client profits drives our goal to be China's top provider of polyolefin and polyethylene compounds. To all our valued clients, we warmly welcome you to visit Zhongchao and witness firsthand the excellence of our high-quality compounds and solutions.
Quality Objectives
Zero defect
On-Time delivery
Zero customer complaint
Quality Policy
Quality Assurance:To satisfy customers' requirements
To achieve"Zero-defect" goal.
Production Management:
Quality is made by production not by Q.C.
Responsibility
Abide by government rules, establish low-emission working condition, reduce pollution in circumstance, improve anti-pollution measures, save energy, reduce percent of defective products, ensure products quality and safety. Make sure water resource clean, keep worker's health to establish perfect healthy policy.
The Mission of R&D center is to create best plastic solutions for Wire & Cable Manufacturers
We have a high-quality research and development team,equipped with complete test equipment testing center and pilot plant, to the greatest extent possible to meet customer demand .
Customized product development
Customised product development depends on your needs. Our new material products are manufactured to meet your technical specifications.
New design and product development
New design and product development is more project-oriented where we create new products with new properties to anticipate and meet future customer trends. There are two new types of compound we are focusing on which can used in Solar battery insulation wire,Shipboard , Telecom Cables and High speed train. It is supposed to be released in the middle of next year.
University Cooperation
Further value will be created via cooperations with customers and universities. We have cooperated with XiAn JiaoTong University and Harbin University of Science and Technology.ZCNM provide annual scholarships and internship opportunities to high performing postgraduate and undergraduate students within these fields. The Innovation Centre will respond to market needs and enhance education and know-how in plastic new material development .The Innovation Centre brings scientists, engineers and technicians together to ensure that Zhongchao products continue to provide the best value to our customers.