Product Type: | Wire |
---|---|
Material: | Fenico |
Carbon Content: | Low Carbon |
PCD: | 98mm |
ET: | 0 |
Hole: | 0 |
Proveedores con licencias comerciales verificadas
Ni | 28.5~29.5 | Fe | Bal. | Co | 16.8~17.8 | Si | ≤0.3 |
Mo | ≤0.2 | Cu | ≤0.2 | Cr | ≤0.2 | Mn | ≤0.5 |
C | ≤0, 03 | P | ≤0, 02 | S | ≤0, 02 |
Código de estado | El estado | El cable | Gaza |
R | Soft | ≤ 585 | ≤ 570 |
1/4I | Duro 1/4 | 585~725 | 520~630 |
1/2I | Duro 1/2 | 655~795 | 590~700 |
3/4I | Duro 3/4 | 725~860 | 600~770 |
I | Hard | ≥850 | ≥700 |
La Densidad (g/cm3). | 8.2. |
La resistividad eléctrica a 20ºC(Om*mm2/m). | 0.48 |
Factor de temperatura de resistividad(20ºC~100ºC)X10-5/ºC | 3.7~3.9 |
Punto de Curie Tc/°C | 430 |
Módulo elástico, E/ Gpa | 138 |
Θ/ºC | Α1/10-6ºC-1 | Θ/ºC | Α1/10-6ºC-1 |
20~60 | 7.8 | 20~500 | 6.2 |
20~100 | 6.4 | 20~550 | 7.1. |
20~200 | 5.9 | 20~600 | 7.8 |
20~300 | 5.3 | 20~700 | 9.2 |
20~400 | 5.1. | 20~800 | 10.2 |
20~450 | 5.3 | 20~900 | 11.4 |
Θ/ºC | 100 | 200 | 300 | 400 | 500 |
Λ / W/(m*ºC) | 20.6 | 21.5 | 22.7 | 23.7 | 25.4 |
El proceso de tratamiento térmico | |
El recocido para alivio de tensión | Calienta a 470~540ºC y mantenga 1~2 h. El frío abajo |
El recocido | En el vacío calienta 750~900ºC |
El tiempo sosteniendo | 14 min~1h. |
Velocidad de enfriamiento | No más de 10 ° C/min enfriado a 200 °C. |
Nombre de aleaciones | Tipo | La dimensión | ||
UALLOY-4J29 | El cable | D= 0.1~8mm | ||
UALLOY-4J29 | Gaza | 5~250W= mm | T= 0.1-3.0mm | |
UALLOY-4J29 | La lámina | W= 10~100mm | T= 0.01~0.1 | |
UALLOY-4J29 | Bar | 8~100Dia= mm | L= 50~1000 |