Proveedor Auditado Welding Wire Er110s-G High Strength Steel Welding Wire Carbon Steel Solid
AWS ER110S-G solid welding wire is a kind of high tensile strengh welding wire, also called mag/mig welding wire which is matched with CO2 gas and Arc gas in welding. It has strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Application: For multi-pass welding of heavy structures made by 760MPa grade high tensile low alloy steels, eg, heavy engeering machines. Preheating temperature and interpass temperature should between 180º C to 190º C and the welded piece should be tempered at 310º C not shorter than 2 hours after welding.
Packing: 5kg/10kg/15kg/20kg/spool in carton, 250kg/ drum, 21.6MT -25.2MT per 1X20" FCL.
| Chemical Composition of Welding Wire (%) | |||||||||||
| C | Mn | Si | S | P | Ti | Ni | Mo | Cu | AL | Zr | |
| 0.074 | 1.76 | 0.47 | 0.004 | ≤0.008 | 0.30 | 2.11 | 0.54 | 0.20 | - | - | |
| Test Item | Rm(MPa) | ReL/Rp0.2(Mpa) | A(%) | KV2(J) -40ºC |
| General Result | 775 | 665 | 23 | 90 CO2(20%) + Ar(80%) |
| Wire Size(mm) | Welding Current (A) | CO2 Flow Rate (L/Min) |
| 0.8 | 50-100 | 15-20 |
| 1.0 | 60-220 | 15-20 |
| 1.2 | 80-350 | 15-25 |
| 1.6 | 170-550 | 20-25 |
However, we can do it as client's request:
Delivery:7-15 days after order confirmed
Other welding consumables available