Bronce fosforado. | |||||||||||||
Composición química(%) | |||||||||||||
Standard | La clase | Aleación | Cu | Al. | Fe | Mn | Ni | P | Pb | Si | Sn | Zn | Otros |
La norma ISO24373 | Cu5210 | CuSn8P | Bal. | - | 0.1 | - | 0.2 |
0.01~ 0.4 |
0.02 | - |
7.5~ 8.5 |
0.2 | 0.2 |
GB/T9460 | La SCu5210 | CuSn8P | Bal. |
- |
Máx. 0.1 |
- |
Máx. 0.2 |
0.01~
0.4 |
Máx. 0.02 |
- |
7.5~ 8.5 |
Máx. 0.2 |
Máx. 0.2 |
BS EN14640 | Cu5210 | CuSn9P | Bal. | - | 0.1 | - | - |
0.01~ 0.4 |
0.02 | - |
7.5~ 9.0 |
0.2 | 0.5 |
La AWS A5.7 | C52100 | ERCuSn-C | Bal. | 0.01 | 0.10 | - | - |
0.10~ 0.35 |
0.02 | - |
7.5~ 9.0 |
0.2 |
0.50 |
Propiedades físicas y propiedades mecánicas: | |||||||||||||
Solid-Temperature | 875ºC | Liquids-Temperature | 1025ºC | ||||||||||
Densidad | 8.8Kg/dm3 | Fuerza tensil | 260N/mm2 | ||||||||||
La elongación | El 20% | Dureza Brinell | 80HB | ||||||||||
Introducción: | |||||||||||||
Recomendado para la soldadura de cobre con aleación Cu-Sn.mejor para el culo de unirse a la soldadura de latón con acero.precalentar sugerido para los productos de gran tamaño, y de impulsos de la soldadura es recomendado para el duro multicapa enfrentando en acero. |
Marca | S213 |
Equivalente a AWS | ERCuSn-C |
Características | Buenas propiedades mecánicas
Buena resistencia a la corrosión
|
Método de soldadura | GTAW
La soldadura
|
Aplicación | Se utiliza para TIG,excelente para el llano o aceros recubiertos.También se utiliza para sufacing arears sometido a corrossion. |
Propiedades físicas y propiedades mecánicas: | |
Solids-Temperature | 875ºC |
Liquids-Temperature | 1025ºC |
Densidad | 8.8Kg/dm3 |
Fuerza tensil | 260N/mm2 |
La elongación | El 20% |
Dureza Brinell | 80HB |