After-sales Service: | Good |
---|---|
Warranty: | According to The Agreement |
Type: | Steel Plate |
Standard: | ASTM, AISI, GB, JIS, DIN, BS |
Certification: | ISO |
Surface Treatment: | Painted/Polished, Normalizing, Anneal |
Proveedores con licencias comerciales verificadas
Especificación de la placa de acero corten | |
Standard El grado |
La norma ASTM: Corten Corten A; B;588Gr.A/Gr.B/Gr.C/ Gr.K; Un242; Un606 tipo 4; UN709 Gr 50W. EN10025: S235J0W, S235J2W, S355J0W, S355J2W, S355K2W, S355J0WP; S355J2WP; S355J2G1W, S355J2G2W, S355K2G1W, S355K2G2W. JIS G3114: SMA400AW; SMA400BW; SMA400CW; SMA490AW; SMA490BW; SMA490CW; SMA570W; SMA570P; JIS G3125: SPA-H; SPA-C; GB/T 4171: Q235NH; Q265GNH; Q310GNH; Q295NH; Q295GNH; Q355NH; Q355GNH; Q415NH; Q460NH; 1500NH; Q550NH; TB/T 1979: 09CuPCrNi CuCrNi; 09-A-B; 05CuPCrNi; Q/BQB 340: B460B490NQR NQR;; B480B600GNQR GNQR;. |
Grosor | Laminados en frío laminados en caliente 2-3000.5-2mm mm (2-100mm utilizado normalmente) |
El ancho | 1000-3000mm (1000-2200mm utilizado normalmente) |
Longitud | 1000-12000mm o como su solicitud |
Superficie | Limpio, limpieza y pintura de acabado, según los requerimientos del cliente |
La entrega Los Estados |
Laminados en caliente, el control de balanceo, normalizar, hibridación, templado, Temple, N+T, Q+T,y la entrega de otros estados están disponibles como sea necesario |
Certificado | API,ISO,SGS,BV,CE... |
La calidad | MTC contará con los bienes, tercera parte de la inspección es aceptable, Por ejemplo BV,SGS. |
Paquete | Paquete de condiciones de navegabilidad de exportación estándar, apto para todo tipo de transporte, O como sea necesario. |
Contenedor El tamaño |
20ft GP:5898mm de longitud()x2352mm(ancho)x2393mm(alto) |
El GP de 40 pies:12032mm(longitud)x2352mm(ancho)x2393mm(alto) | |
El comercio plazo | Ex-Work,FOB,CNF, CFR, CIF,etc. |
Aplicación | Ampliamente utilizado en una variedad de estructuras de arquitectura e ingeniería, tales como 1) construcciones metálicas tales como edificios, puentes, barcos. 2.) de la torre de transmisión de la torre, la reacción. 3) transporte de maquinaria de elevación. 4.) de hornos industriales calderas; 5.) marco de contenedor de almacén, estantes de las mercancías, etc. |
Placa de acero corten composición química y propiedades mecánicas |
||||||||
El grado | C | Si | Mn | P | S | Cr | Ni | Cu |
CORTEN UN | ≤0,12 | 0.25-0,75 | 0.20-0.50 | 0.07-0,15 | ≤ 0.030 | 0.50-1.25 | ≤0,65 | 0.25 -0.55 |
CORTEN B | ≤0,16 | 0.30-0.50 | 0.80-1.25 | 0.030 | ≤ 0.030 | 0.40-0.65 | 0.40 | 0.25 -0.40 |
El grado |
Límite de fluencia MPA | Fuerza tensil MPA | La elongación % |
CORTEN UN | ≥355 | 470-630 | ≥20 |
CORTEN B | ≥345 | 470-630 | ≥20 |
El grado | C | Mn | Cr | Si | N | S | Cu | P | Ni | V | ||||||||||
Una588GRA | ≤0,19 | 0.80-1.25 | 0.40-0.65 | 0.30- 0.65 |
≤ 0.010 | 0.050 | 0.25-0.40 | 0.040 | ≤0,40 | 0. 01 -0. 10 |
||||||||||
Una588GrB | ≤0,20 | 0,75-1,35 | 0.40-0.70 | 0.15- 0.50 |
≤ 0.010 | 0.050 | 0.20-0.40 | 0.040 | ≤0,50 | 0. 01 -0. 10 |
||||||||||
El GrC588 | ≤0,15 | 0.80-1.35 | 0.30-0.50 | 0.15- 0.30 |
≤ 0.010 | 0.050 | 0.20-0.50 | 0.040 | 0.25-0.50 | 0.0 1- 0. 10 |
||||||||||
Material | El grado | Composición química,% | ||||||||||||||||||
C | Si | Mn | P | S | Cu | Cr | Ni | V | ||||||||||||
P235NH | A-E | ≤ 0.13 | 0.10-0.40 | 0.20-0,60 | ≤ 0.13 | ≤ 0.13 | 0.25-0.55 | 0.40-0,80 | ≤ 0,65 | / | ||||||||||
P295NH | A-E | ≤0,15 | 0.10-0.50 | 0.60-1.00 | ≤ 0.13 | ≤ 0.13 | 0.25-0.55 | 0.40-0,80 | ≤ 0,65 | / | ||||||||||
P295GNH | A-E | ≤ 0.12 | 0.10-0.40 | 0.20-0.50 | ≤ 0.13 | ≤ 0.13 | 0.25-0.55 | 0.40-0,80 | 0.25 -0.50 |
/ | ||||||||||
P355NH | A-E | ≤ 0.16 | ≤ 0,50 | 0.50-1.50 | ≤ 0.13 | ≤ 0.13 | 0.25-0.55 | 0.40-0,80 | ≤ 0,65 | / | ||||||||||
P355GNH | A-E | ≤ 0.12 | 0.20-0,75 | ≤ 1.00 | ≤ 0.13 | ≤ 0.13 | 0.25-0.55 | 0.40-0,80 | ≤ 0,65 | / | ||||||||||
09CuPCrNi-A | / | ≤ 0.12 | 0.20-0,75 | 0.20-0.50 | 0.060-0.12 | ≤ 0.020 | 0.25-0.50 | 0.30-1.25 | 0.12 0,65 |
/ | ||||||||||
09CuPCrNi-B | / | ≤ 0.12 | 0.10-0.40 | 0.20-0.50 | 0.060-0.12 | ≤ 0.020 | 0.25-0.50 | 0.30-0.65 | 0.25 -0.50 |
/ | ||||||||||
05CuPCrNi | / | ≤ 0.090 | 0.25-0.50 | 0.20-0.50 | 0.060-0.12 | ≤ 0.020 | 0.25-0.50 | 0.30-1.25 | 0.12 0,65 |
/ | ||||||||||
B480GNQR | / | ≤ 0.12 | 0.25-0,75 | 0.20-0.50 | 0.070-0,15 | ≤ 0.030 | 0.25-0.55 | 0.30-1.25 | ≤ 0,65 | / | ||||||||||
P450NQR1 | / | ≤ 0.12 | ≤ 0.75 | ≤ 1.50 | ≤ 0.025 | ≤ 0.020 | 0.20-0.55 | 0.30-1.25 | ≤ 0,65 | / | ||||||||||
SPA-H | / | 0.05-0.12 | 0.25-0,75 | 0.20-0,60 | 0.070-0.12 | ≤ 0.025 | 0.25-0.50 | 0.30-1.25 | ≤ 0,65 | / |
El grado | C | Mn | Cr | Si | CEV | S | Cu | P | |||
S355J2WP | ≤0,12 | ≤1,00 | 0.3-1.25 | ≤0,75 | ≤0,52 | ≤0,03 | 0.25-0.55 | 0.06 - 0,15 |
|||
El grado | Límite de fluencia MPA | Fuerza tensil MPA | Impacto | ||||||||
De espesor mm | ≤16 | >16 ≤40 |
>40 ≤ 150 |
≤3 | >3 ≤ 100 | >100 ≤ 150 | Grado | J | |||
S355J2WP | ≥355 | ≥345 | - | 510-680 | 470-630 | - | -20 | 27 |
%C | %Si | %Mn | %P | %S. | %Cr | %Cu | %V | %Ni | El rendimiento | Resistencia | La elongación | |
Corten un | 12. | .25-.75 | .2-5. | .07-15. | .03 | .5-1.25 | .25-.55 | 65 | 355MPA | 470-630MPA | El 20% | |
Corten B | 16. | .3-5. | .8-1.25 | .03 | .03 | .4-65 | .25-4. | .02-1. | 4. | 355MPA | 470-630MPA | El 20% |
ASTM A588 | 19. | .3-65 | .8-1.25 | .05 | .04 | .4-65 | .25-4. | 4. | 340MPA | 480MPA | ||
ASTM A242 TIPO 1 | 12. | .75 | 1 | .06-15. | .03 | .3-1.25 | .25-.55 | 52. | 4. | 355MPA | 510-680 | Impacto-20/27J |
S355JOWP | 12. | .75 | 1 | .06-15. | .035 | .3-1.25 | .25-.55 | N.009 | 4. | 355MPA | 510-680 | Impacto0/27J |